Making Cupric Chloride Etchant

By: Erik L. Knise
spamelknise~NOSPAM~ at -Remove-gmail.com

When etching a board with Cupric Chloride it really doesn't matter what strength we use as long as we have the correct proportions of H2O2 (hydrogen peroxide) and HCL (hydrochloric acid). We only need enough volume to cover our board. A stronger solution would be easier to store as regenerating with weak H2O2 and HCL would increase the volume greatly. Starting off with weak H2O2 and HCL should be sufficent for most small runs.

This is how our reaction works:

First we are making Cupric Chloride (CuCl2):
Cu + H2O2 + 2HCl -> 2H2O + CuCl2

The Copper reacts with the CuCl2 from the previous reaction to form Cuprous Chloride (CuCl):
Cu + CuCl2 -> 2CuCl

The Cuprous Chloride continues to react with the H2O2 and HCL to continue the reaction.
2CuCl + H2O2 + 2HCL -> 2H2O + 2CuCl2

It's a chain reaction and these reactions are all happening simultaneously but each mole of HCl used dissolves 1 mole of copper.

H2O2 has a molecular mass of 34.0147 grams/mole and HCL is 36.46 grams/mole. With 100 grams of 3% H2O2 we would have 3 grams or 0.088 moles of H2O2 (3 grams divided by 34 grams/mole). We would need 0.176 moles of HCl for the reaction. That would be 0.176 moles x 36.5 grams/mole = 6.42 grams. With 27% HCl that would be 6.42 divided by 27% equals 23.78 grams of 27% HCl Solution. 23.78 grams of HCl per 100 grams of H2O2 would be a 1:4.2 ratio. This would of course change with different concentrations.

Solution 1 (H2O2):
Density (g/mol):
Concentration (wt%):
Solution 2 (HCL):
Density (g/mol):
Concentration (wt%):
The Reaction:
Ratio of Sol. 1 to Sol. 2:
Mass of Solution 1 (grams):
Moles of Solution 1 (moles):
Mass of Solution 2 (grams):
Moles of Solution 2 (moles):
Mass Ratio:
The Results:
Moles of Copper Dissolved (moles):
Mass of Copper Dissolved (grams):
Mass of Copper Dissolved (oz):

When regenerating our solution by adding more H2O2 and HCl we are adding it to a solution of CuCl and water. The reaction above starts with 114.374 grams of water and generates another 3.178 grams of water so we have roughly 117.5mL of water when the reaction is complete. This is why to regenerate the etchant it would be best to use more concentrated chemicals so it doesn't get too diluted. If the reaction doesn't use up all of the H2O2 and HCL the H2O2 will break down in the light to H2O and O2 so regenerating with only H2O2 may work. Add H2O2 to the CuCL and water solution first. If the reaction starts there was HCL left in the solution. When adding H2O2 causes no results it's time to add proportionate amounts of both H2O2 and HCl to continue the reaction.

Sources:

http://en.wikipedia.org/wiki/Hydrochloric_acid
http://en.wikipedia.org/wiki/Hydrogen_peroxide
http://en.wikipedia.org/wiki/Copper(I)_chloride
http://en.wikipedia.org/wiki/Copper

Last updated 03/09/11 @ 2035 PST

See also:

Questions:


file: /Techref/pcb/etch/CuCl2Calc.htm, 8KB, , updated: 2016/3/7 14:58, local time: 2024/10/4 07:46,
TOP NEW HELP FIND: 
44.222.134.250:LOG IN
©2024 PLEASE DON'T RIP! THIS SITE CLOSES OCT 28, 2024 SO LONG AND THANKS FOR ALL THE FISH!

 ©2024 These pages are served without commercial sponsorship. (No popup ads, etc...).Bandwidth abuse increases hosting cost forcing sponsorship or shutdown. This server aggressively defends against automated copying for any reason including offline viewing, duplication, etc... Please respect this requirement and DO NOT RIP THIS SITE. Questions?
Please DO link to this page! Digg it! / MAKE!

<A HREF="http://www.sxlist.com/techref/pcb/etch/CuCl2Calc.htm"> Cupric Chloride Etchant Explained and Calculated</A>

After you find an appropriate page, you are invited to your to this massmind site! (posts will be visible only to you before review) Just type a nice message (short messages are blocked as spam) in the box and press the Post button. (HTML welcomed, but not the <A tag: Instead, use the link box to link to another page. A tutorial is available Members can login to post directly, become page editors, and be credited for their posts.


Link? Put it here: 
if you want a response, please enter your email address: 
Attn spammers: All posts are reviewed before being made visible to anyone other than the poster.
Did you find what you needed?

 

Welcome to sxlist.com!


Site supported by
sales, advertizing,
& kind contributors
just like you!

Please don't rip/copy
(here's why

Copies of the site on CD
are available at minimal cost.
 

Welcome to www.sxlist.com!

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

  .